Sachiya Steel International is one of the prominent Manufacture And Exporter in Alloy 20 Angle, Channel, Beam, Chain, which cannot be hardened by heat treatment. The austenitic stainless steels such as Alloy 20 Angle are considered to be the most weldable of the high – alloy steels and can be welded by all fusion and resistance welding processes. Alloy 20 C-Channel is annealed in the 1600 Degree F – 1650 Degree F (871 Degree C – 899 Degree C) range and then air cooled to relieve cold working stresses.
Alloy 20 Chain should not be exposed to temperatures of 2000 Degree F (1093 Degree C) or above due to embrittlement. If excessive large grains are encountered after annealing mildly cold – worked material, the annealing temperature of Alloy 20 H-Beam should be decreased to a range of 1200 Degree F – 1350 Degree F (649 Degree C – 732 Degree C) range.
For maximum corrosion resistance to chemical environments, it is essential that the surface of Alloy 20 T-Beam be free of all heat tint or oxide formed during annealing or hot working. Alloy 20 I-Beam should be machined in the annealed condition using surface speeds. All surfaces of Carpenter 20 Angle must be ground or polished to remove any traces of oxide and surface decarburization. The parts of Carpenter 20 Chain should then be immersed in a warm solution of 10 % – 20 % nitric acid followed by a water rinse to remove any residual iron.
Alloy 20 Angle, Channel, Beam, Chain Specifications |
||
| Specifications | : | ASTM B473 / ASME B473 |
| Dimensions | : | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Alloy 20 Angle |
: | 5mm to 9mm |
| Alloy 20 Channel |
: | 40mm*20mm~300mm*300mm |
| Alloy 20 Beam | : | 3″ thru 12.31″ |
| Alloy 20 Chain |
: | 1/8 inch – 1/2 inch Diameter |
| Thickness |
: | 3.0mm – 120mm |
| Length | : | 3MTR, 4MTR, 5MTR, 6MTR, or Custom Cut Sizes |
| Type | : | Angle, C Channel, U Channel, H Beam, I Beam, T Beam, W Beam, Chain |
Alloy 20 Angle, Channel, Beam, Chain Chemical Composition
| Grade | C | Mn | Si | Cu | Fe | Ni | S | Mo | Cr |
| Alloy 20 | 0.02 max | 1.0-2.0 | 0.7 max | 3.0-4.0 | bal | 32 – 38 | 0.005 max | 2.0-3.0 | 19 – 21 |
Alloy 20 Angle, Channel, Beam, Chain Mechanical Properties
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.1 g/cm3 | 1443 °C (2430 °F) | Psi – 80000 , MPa – 551 | Psi – 35000 , MPa – 241 | 30 % |
Equivalent Grades for Alloy 20 Angle, Channel, Beam, Chain
| STANDARD | WERKSTOFF NR. | UNS | AFNOR | EN |
| Alloy 20 | 2.4660 | N08020 | Z2NCUD31-20AZ | NiCr20CuMo |
Alloy 20 Angle, Channel, Beam, Chain Application Industries
- Off-Shore Oil Drilling Companies
- Power Generation
- Petrochemicals
- Gas Processing
- Specialty Chemicals
- Pharmaceuticals
- Pharmaceutical Equipment
- Chemical Equipment
- Sea Water Equipment
- Heat Exchangers
- Condensers
- Pulp and Paper Industry
Sachiya Steel International is one of the pioneer Manufacture And exporter of Alloy A286 Angle, which is an iron – nickel – chromium alloy with additions of molybdenum and titanium.
Alloy A286 Angle is designed for applications requiring high strength and good corrosion resistance at temperatures up to 704 Degree C. Alloy A286 C-Channel is age – harden able, iron – nickel – chromium super – alloy appropriate for applications that require high tensile strength, oxidation resistance and corrosion resistance.Alloy A286 Chain is a precipitation hardening, austenitic stainless steel designed for use at temperatures up to 1300 Degree F, where high tensile strength, excellent creep strength and good corrosion resistance are required.
Alloy A286 I-Beam is an age – harden able iron base super – alloy for applications requiring high strength from -320 Degree F for up to 1000 Degree F long time, 1300 Degree F – 1500 Degree F short time.
Alloy A286 H-Beam is an iron – based super – alloy useful for applications requiring high strength and corrosion resistance and for lower stress applications at higher temperatures.Alloy A286 Angle | Alloy A286 Angle | Alloy A286 Angle | Alloy A286 Angle | Alloy A286 Angle | Alloy A286 Angle | Alloy A286 Angle | Alloy A286 AngleAlloy A286 T-Beam has excellent fabrication characteristics and high mechanical properties due to age – hardenability.
The limiting chemical composition is excellent, where A286 Alloy Angle is austenitic in all metallurgical conditions.
A286 Alloy C-Channel is designed for applications requiring high strength and good corrosion resistance.
Sachiya Steel International holds expertise in offering our clients an exceptional array of Alloy 20 Threaded Forged Fittings that is acclaimed for high quality and wide applications.
Due to its nickel, chromium, molybdenum and copper levels, our Alloy 20 Forged Threaded Elbow(UNS N08020) is ideal for use in corrosive environments.
These Alloy 20 Forged Threaded Tee, which also includes copper and molybdenum, is popular in the production of gasoline, solvents, explosives, chemicals, pharmaceuticals and food and synthetic materials.Restricted carbon plus columbium stabilization in our Alloy 20 Forged Threaded Cross permits welded fabrications to be used in corrosive environments, normally without post – weld heat treatment.
Meanwhile, these Alloy 20 Forged Threaded Cap are also being offered in different sizes and shapes to our customers, where we also offer the same at best prices.
So, depending on who you talk to this alloy may be referred to as our Alloy 20 Forged Threaded Fittings or as a nickel alloy, where either way it is still great for corrosion resistance.Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings These Alloy 20 Forged Threaded Coupling is often chosen to solve stress corrosion cracking problems, which may occur with 316L stainless.
Our Alloy 20 Forged Threaded Union of the same name with the designation “Cb-3” indicates Columbium stabilized.
Sachiya Steel International holds expertise in offering our clients an exceptional array of Alloy 20 Threaded Forged Fittings that is acclaimed for high quality and wide applications.
Due to its nickel, chromium, molybdenum and copper levels, our Alloy 20 Forged Threaded Elbow(UNS N08020) is ideal for use in corrosive environments.
These Alloy 20 Forged Threaded Tee, which also includes copper and molybdenum, is popular in the production of gasoline, solvents, explosives, chemicals, pharmaceuticals and food and synthetic materials.Restricted carbon plus columbium stabilization in our Alloy 20 Forged Threaded Cross permits welded fabrications to be used in corrosive environments, normally without post – weld heat treatment.
Meanwhile, these Alloy 20 Forged Threaded Cap are also being offered in different sizes and shapes to our customers, where we also offer the same at best prices.
So, depending on who you talk to this alloy may be referred to as our Alloy 20 Forged Threaded Fittings or as a nickel alloy, where either way it is still great for corrosion resistance.Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged Fittings | Alloy 20 Threaded Forged FittingsThese Alloy 20 Forged Threaded Coupling is often chosen to solve stress corrosion cracking problems, which may occur with 316L stainless.
Our Alloy 20 Forged Threaded Union of the same name with the designation “Cb-3” indicates Columbium stabilized.
Sachiya Steel International is one of the prominent Manufacture & exporter in Incoloy Alloy 20 Tube to Female Pipes, which is commercially pure (99.6 %) wrought nickel.
Alloy 20 Tube Fittings is normally limited to service at temperatures below 600 Degree F. At higher temperatures, Alloy 20 Compression Fittings can suffer from graphitization which can result in severely compromised properties.
All hot working and cold working practices can be utilized when shaping Alloy 20 Female Connector Fittings.
Hot working temperatures for Alloy 20 Ferrule Fittings should be between 1200 Degree F and 2250 Degree F with heavy forming to be performed at temperatures above 1600 Degree F.Annealing of Alloy 20 Double Ferrule Fittings should be performed at a temperature between 1300 Degree F and 1600 Degree F. Care should be taken when choosing the anneal temperature and time at temperature for Carpenter 20 Compression Tube Fittings can greatly influence the mechanical properties and structure of the material.
When operating temperatures are expected to exceed 600 Degree F, carbon content in Carpenter 20 Female Connector Fittings becomes critical.Incoloy Alloy 20 Tube to Female Pipes | Incoloy Alloy 20 Tube to Female Pipes | Incoloy Alloy 20 Tube to Female Pipes | Incoloy Alloy 20 Tube to Female Pipes | Incoloy Alloy 20 Tube to Female Pipes | Incoloy Alloy 20 Tube to Female Pipes | Incoloy Alloy 20 Tube to Female Pipes | Incoloy Alloy 20 Tube to Female PipesThe lower carbon content of Carpenter 20 Tube Fittings makes the material resistant to graphitization and therefore less subject to embrittlement.
Carpenter 20 Compression Fittings is approved for construction of pressure vessels and components under ASME Boiler and Pressure Vessel Code Section VIII, Division 1.